Yield surface


A yield surface is a five-dimensional surface in the six-dimensional space of stresses. The yield surface is usually convex and the state of stress of inside the yield surface is elastic. When the stress state lies on the surface the material is said to have reached its yield point and the material is said to have become plastic. Further deformation of the material causes the stress state to remain on the yield surface, even though the shape and size of the surface may change as the plastic deformation evolves. This is because stress states that lie outside the yield surface are non-permissible in rate-independent plasticity, though not in some models of viscoplasticity.
The yield surface is usually expressed in terms of a three-dimensional principal stress space, a two- or three-dimensional space spanned by stress invariants or a version of the three-dimensional Haigh–Westergaard stress space. Thus we may write the equation of the yield surface in the forms:
The first principal invariant of the Cauchy stress, and the second and third principal invariants of the deviatoric part of the Cauchy stress are defined as:
where are the principal values of, are the principal values of, and
where is the identity matrix.
A related set of quantities,, are usually used to describe yield surfaces for cohesive frictional materials such as rocks, soils, and ceramics. These are defined as
where is the equivalent stress. However, the possibility of negative values of and the resulting imaginary makes the use of these quantities problematic in practice.
Another related set of widely used invariants is which describe a cylindrical coordinate system. These are defined as:
The plane is also called the Rendulic plane. The angle is called the Lode angle and the relation between and was first given by Nayak and Zienkiewicz in 1972
The principal stresses and the Haigh–Westergaard coordinates are related by
A different definition of the Lode angle can also be found in the literature:
in which case the ordered principal stresses are related by

Examples of yield surfaces

There are several different yield surfaces known in engineering, and those most popular are listed below.

Tresca yield surface

The Tresca yield criterion is taken to be the work of Henri Tresca. It is also known as the maximum shear stress theory and the Tresca–Guest criterion. In terms of the principal stresses the Tresca criterion is expressed as
Where is the yield strength in shear, and is the tensile yield strength.
Figure 1 shows the Tresca–Guest yield surface in the three-dimensional space of principal stresses. It is a prism of six sides and having infinite length. This means that the material remains elastic when all three principal stresses are roughly equivalent, no matter how much it is compressed or stretched. However, when one of the principal stresses becomes smaller than the others the material is subject to shearing. In such situations, if the shear stress reaches the yield limit then the material enters the plastic domain. Figure 2 shows the Tresca–Guest yield surface in two-dimensional stress space, it is a cross section of the prism along the plane.

von Mises yield surface

The von Mises yield criterion is expressed in the principal stresses as
where is the yield strength in uniaxial tension.
Figure 3 shows the von Mises yield surface in the three-dimensional space of principal stresses. It is a circular cylinder of infinite length with its axis inclined at equal angles to the three principal stresses. Figure 4 shows the von Mises yield surface in two-dimensional space compared with Tresca–Guest criterion. A cross section of the von Mises cylinder on the plane of produces the elliptical shape of the yield surface.

Burzyński-Yagn criterion

This criterion
represents the general equation of a second order surface of revolution about the hydrostatic axis. Some special case are:
The relations compression-tension and torsion-tension can be computed to
The Poisson's ratios at tension and compression are obtained using
For ductile materials the restriction
is important. The application of rotationally symmetric criteria for brittle failure with
has not been studied sufficiently.
The Burzyński-Yagn criterion is well suited for academic purposes. For practical applications, the third invariant of the deviator in the odd and even power should be introduced in the equation, e.g.:

Mohr–Coulomb yield surface

The Mohr–Coulomb yield criterion is similar to the Tresca criterion, with additional provisions for materials with different tensile and compressive yield strengths. This model is often used to model concrete, soil or granular materials. The Mohr–Coulomb yield criterion may be expressed as:
where
and the parameters and are the yield stresses of the material in uniaxial compression and tension, respectively. The formula reduces to the Tresca criterion if.
Figure 5 shows Mohr–Coulomb yield surface in the three-dimensional space of principal stresses. It is a conical prism and determines the inclination angle of conical surface. Figure 6 shows Mohr–Coulomb yield surface in two-dimensional stress space. It is a cross section of this conical prism on the plane of.

Drucker–Prager yield surface

The Drucker–Prager yield criterion is similar to the von Mises yield criterion, with provisions for handling materials with differing tensile and compressive yield strengths. This criterion is most often used for concrete where both normal and shear stresses can determine failure. The Drucker–Prager yield criterion may be expressed as
where
and, are the uniaxial yield stresses in compression and tension respectively. The formula reduces to the von Mises equation if.
Figure 7 shows Drucker–Prager yield surface in the three-dimensional space of principal stresses. It is a regular cone. Figure 8 shows Drucker–Prager yield surface in two-dimensional space. The elliptical elastic domain is a cross section of the cone on the plane of ; it can be chosen to intersect the Mohr–Coulomb yield surface in different number of vertices. One choice is to intersect the Mohr–Coulomb yield surface at three vertices on either side of the line, but usually selected by convention to be those in the compression regime. Another choice is to intersect the Mohr–Coulomb yield surface at four vertices on both axes or at two vertices on the diagonal . The Drucker-Prager yield criterion is also commonly expressed in terms of the material cohesion and friction angle.

Bresler–Pister yield surface

The Bresler–Pister yield criterion is an extension of the Drucker Prager yield criterion that uses three parameters, and has additional terms for materials that yield under hydrostatic compression.
In terms of the principal stresses, this yield criterion may be expressed as
where are material constants. The additional parameter gives the yield surface an ellipsoidal cross section when viewed from a direction perpendicular to its axis. If is the yield stress in uniaxial compression, is the yield stress in uniaxial tension, and is the yield stress in biaxial compression, the parameters can be expressed as

Willam–Warnke yield surface

The Willam–Warnke yield criterion is a three-parameter smoothed version of the Mohr–Coulomb yield criterion that has similarities in form to the Drucker–Prager and Bresler–Pister yield criteria.
The yield criterion has the functional form
However, it is more commonly expressed in Haigh–Westergaard coordinates as
The cross-section of the surface when viewed along its axis is a smoothed triangle. The Willam–Warnke yield surface is convex and has unique and well defined first and second derivatives on every point of its surface. Therefore, the Willam–Warnke model is computationally robust and has been used for a variety of cohesive-frictional materials.

Podgórski and Rosendahl trigonometric yield surfaces

Normalized with respect to the uniaxial tensile stress, the Podgórski criterion as function of the stress angle reads
with the shape function of trigonal symmetry in the -plane
It contains the criteria of von Mises, Tresca, Mariotte, Ivlev and also the cubic criterion of Sayir with and the isotoxal hexagons of the Capurso criterion with. The von Mises - Tresca transition follows with,. The isogonal hexagons of the Haythornthwaite criterion containing the Schmidt-Ishlinsky criterion cannot be described with the Podgórski ctiterion.
The Rosendahl criterion reads
with the shape function of hexagonal symmetry in the -plane
It contains the criteria of von Mises, Tresca, Schmidt--Ishlinsky, Sokolovsky, and also the bicubic criterion of Szwed with or equally with and the isotoxal dodecagons of the unified yield criterion of Yu with. The isogonal dodecagons of the multiplicative ansatz criterion of hexagonal symmetry containing the Ishlinsky-Ivlev criterion cannot be described by the Rosendahl criterion.
The criteria of Podgórski and Rosendahl describe single surfaces in principal stress space without any additional outer contours and plane intersections. Note that in order to avoid numerical issues the real part function can be introduced to the shape function: and. The generalization in the form is relevant for theoretical investigations.
A pressure-sensitive extension of the criteria can be obtained with the linear -substitution
which is sufficient for many applications, e.g. metals, cast iron, alloys, concrete, unreinforced polymers, etc.

Bigoni–Piccolroaz yield surface

The Bigoni–Piccolroaz yield criterion is a seven-parameter surface defined by
where is the "meridian" function
describing the pressure-sensitivity and is the "deviatoric" function
describing the Lode-dependence of yielding. The seven, non-negative material parameters:
define the shape of the meridian and deviatoric sections.
This criterion represents a smooth and convex surface, which is closed both in hydrostatic tension and compression and has a
drop-like shape, particularly suited to describe frictional and granular materials. This criterion has also been generalized to the case of surfaces with corners.

Cosine Ansatz (Altenbach-Bolchoun-Kolupaev)

For the formulation of the strength criteria the stress angle
can be used.
The following criterion of isotropic material behavior
contains a number of other well-known less general criteria, provided suitable parameter values are chosen.
Parameters and describe the geometry of the surface in the -plane. They are subject to the constraints
which follow from the convexity condition. A more precise formulation of the third constraints is proposed in.
Parameters and describe the position of the intersection points of the yield surface with hydrostatic axis. These intersections points are called hydrostatic nodes.
In the case of materials which do not fail at hydrostatic pressure one gets. Otherwise for materials which fail at hydrostatic pressure it follows.
The integer powers and, describe the curvature of the meridian. The meridian with is a straight line and with – a parabola.

Barlat's Yield Surface

For the anisotropic materials, depending on the direction of the applied process the mechanical properties vary and, therefore, using an anisotropic yield function is crucial. Since 1989 Frederic Barlat has developed a family of yield functions for constitutive modelling of plastic anisotropy. Among them, Yld2000-2D yield criteria has been applied for a wide range of sheet metals. The Yld2000-2D model is a non-quadratic type yield function based on two linear transformation of the stress tensor:
for principal values of X’ and X”, the model could be expressed as:
and:
where are eight parameters of the Barlat's Yld2000-2D model to be identified with a set of experiments.