Palliser shot was invented by Sir William Palliser and hence its name. It was an early British armour-piercing artillery projectile, intended to pierce the armour protection of warships being developed in the second half of the 19th century.
History
Major Palliser's shot, approved 21 October 1867, was an improvement over the ordinary elongated shot of the time. It was adopted for the larger types of rifled muzzle-loading guns rifled on the Woolwich principle. Palliser shot in many calibers stayed in service in the armour-piercing role until phased out of service in 1909 for naval and fortress use, and 1921 for land service.
Palliser shot
Palliser shot was made of cast iron, the head being chilled in casting to harden it, using composite molds with a metal, water-cooled portion for the head. At times there were defects that led to cracking in the projectiles, but these were overcome with time. Bronze studs were installed into the outside of the projectile so as to engage the rifling grooves in the gun barrel. The base had a hollow pocket but was not filled with powder or explosive: the cavity was necessitated by difficulties in casting large solid projectiles without their cracking when they cooled, because the nose and base of the projectiles cooled at different rates, and in fact a larger cavity facilitated a better-quality casting. The hole at the base was threaded to accept a copper gas check. This prevented propellant gases from blowing around the projectile, providing obturation as the driving band had yet to be perfected. Later designs did away with the studs on the projectile body, with the gas checks being set with grooves to impart spin to the projectile. At the Battle of Angamos the Chilean ironclad warshipsfired twenty 250-pound Palliser gunshots against the Peruvian monitor Huáscar, with devastating results. It was the first time that such piercing shells were used in actual combat.
Britain also deployed Palliser shells in the 1870s–1880s. In the shell the cavity was slightly larger than in the shot and was filled with gunpowder instead of being empty, to provide a small explosive effect after penetrating armour plating. The shell was correspondingly slightly longer than the shot to compensate for the lighter cavity. The powder filling was ignited by the shock of impact and hence did not require a fuze. While these Palliser shells were effective against unhardened iron, British doctrine held that only shot were suitable for penetrating the new hardened armour being developed in the 1880s; hence the gunpowder filling was discontinued.